Abstract The aim of this study was to evaluate the influence of adding quaternary ammonium methacrylates (QAMs) to experimental adhesives by assessing the degree of conversion (DC), cytotoxicity against keratinocytes and fibroblasts, and antibacterial activity against biofilm formation. Two QAMs were added to an experimental adhesive: dimethylaminododecyl methacrylate bromododecane (DMADDM) or dimethylaminododecyl methacrylate bromohexadecane (DMAHDM) at three concentrations each: 1, 2.5, and 5 wt.%. Experimental adhesive without QAMs (control group) and commercially available Transbond XT Primer (3M Unitek, Monrovia, California, USA) were used for comparisons. The adhesives were tested for DC, cytotoxicity against keratinocytes and fibroblasts, and antibacterial activity against biofilm formation. DC, cytotoxicity against fibroblasts, and antibacterial activity were analyzed using one-way ANOVA and Tukey’s multiple comparisons. Cytotoxicity against keratinocytes was evaluated using the Kruskal Wallis and Dunn’s post-hoc (α = 5%) tests. Transbond showed lower DC as compared to 5% DMAHDM, 1% DMADDM, and 5% DMADDM (p < 0.05). However, all groups presented proper DC when compared to commercial adhesives in the literature. In the evaluation of cytotoxicity against keratinocytes, Transbond induced higher viability than 2.5 wt.% groups (p < 0.05). Against fibroblasts, Transbond induced higher viability as compared to 5 wt.% groups (p < 0.05). DMAHDM at 5 wt.% reduced biofilm formation when compared to all the other groups (p < 0.05). Despite their cytotoxic effect against keratinocytes, gingival fibroblasts showed higher viability. DMAHDM at 5 wt.% decreased Streptococcus mutans viability. The incorporation of DMAHDM at 5 wt.% may be a strategy for reducing the development of white spot lesions.

Abstract Fixed orthodontic appliances may lead to biofilm accumulation around them that may increase caries risk. This study aimed to evaluate the influence of quaternary ammonium methacrylates (QAMs) on the physicochemical properties, cytotoxicity, and antibacterial activity of adhesive resins for orthodontic purposes. Methodology: A base resin was prepared with a comonomer blend and photoinitiator/co-initiator system. Two different QAMs were added to the base adhesive: dimethylaminododecyl methacrylate at 5 wt.% (DMADDM) or dimethylaminohexadecyl methacrylate (DMAHDM) at 10 wt.%. The base adhesive, without QAMs, (GC) and the commercial Transbond™ XT Primer 3M (GT) were used as control. The resins were tested immediately and after six months of aging in the water regarding the antibacterial activity and shear bond strength (SBS). The antibacterial activity was tested against Streptococcus mutans via metabolic activity assay (MTT test). The groups were also tested for the degree of conversion (DC) and cytotoxicity against keratinocytes. Results: The resins containing QAM showed antibacterial activity compared to the commercial material by immediately reducing the metabolic activity by about 60%. However, the antibacterial activity decreased after aging (p<0.05). None of the groups presented any differences for SBS (p>0.05) and DC (p>0.05). The incorporation of DMADDM and DMAHDM significantly reduced the keratinocyte viability compared to the GT and GC groups (p<0.05). Conclusion: Both adhesives with QAMs showed a significant reduction in bacterial metabolic activity, but this effect decreased after water aging. Lower cell viability was observed for the group with the longer alkyl chain-QAM, without significant differences for the bonding ability and degree of conversion. The addition of QAMs in adhesives may affect the keratinocytes viability, and the aging effects maybe decrease the bacterial activity of QAM-doped materials.

Abstract The aim of this study was to evaluate the influence of polyhexamethylene guanidine hydrochloride (PHMGH) in the physico-chemical properties and antibacterial activity of an experimental resin sealant. An experimental resin sealant was formulated with 60 wt.% of bisphenol A glycol dimethacrylate and 40 wt.% of triethylene glycol dimethacrylate with a photoinitiator/co-initiator system. PHMGH was added at 0.5 (G0.5%), 1 (G1%), and 2 (G2%) wt.% and one group remained without PHMGH, used as control (GCTRL). The resin sealants were analyzed for degree of conversion (DC), Knoop hardness (KHN), and softening in solvent (ΔKHN), ultimate tensile strength (UTS), contact angle (θ) with water or α-bromonaphthalene, surface free energy (SFE), and antibacterial activity against Streptococcus mutans for biofilm formation and planktonic bacteria. There was no significant difference for DC (p > 0.05). The initial Knoop hardness ranged from 17.30 (±0.50) to 19.50 (± 0.45), with lower value for GCTRL (p < 0.05). All groups presented lower KHN after immersion in solvent (p < 0.05). The ΔKHN ranged from 47.22 (± 4.30) to 57.22 (± 5.42)%, without significant difference (p > 0.05). The UTS ranged from 54.72 (± 11.05) MPa to 60.46 (± 6.50) MPa, with lower value for G2% (p < 0.05). PHMGH groups presented no significant difference compared to GCTRL in θ (p > 0.05). G2% showed no difference in SFE compared to GCTRL (p > 0.05). The groups with PHMGH presented antibacterial activity against biofilm and planktonic bacteria, with higher antibacterial activity for higher PHMGH incorporation (p < 0.05). PHMGH provided antibacterial activity for all resin sealant groups and the addition up to 1 wt.% showed reliable physico-chemical properties, maintaining the caries-protective effect of the resin sealant over time.

Resumo O objetivo desse estudo foi desenvolver e avaliar a adição de 1,3,5-triacryloylhexahydro-1,3,5-triazine a uma resina adesiva experimental em diferentes concentrações. Resinas adesivas experimentais foram obtidas a partir da mistura de 50% em peso de bisphenol A glycol dimethacrylate (BisGMA), 25% em peso de triethylene glycol dimethacrylate (TEGDMA), 25% em peso de hidroxietil metacrilato (HEMA) e sistema fotoiniciador. O composto de triazina foi adicionado em proporções de 1; 2,5 e 5% em peso a resina adesiva base e um grupo permaneceu sem a adição do composto de triazina como grupo controle. As resinas adesivas experimentais foram analisadas por atividade antibacteriana (n=3), grau de conversão (n=3) e degradação em solvente (n=3). A distribuição dos dados foi avaliada por teste de Kolmogorov-Smirnov, teste t pareado, ANOVA de uma via e Tukey, considerando nível de significância de 5%. Todos os grupos com adição de composto de triazina demonstraram atividade antibacteriana contra Streptococcus mutans (p<0,05). Todos os grupos atingiram mais de 70% de grau de conversão, mas não houve diferença estatística para essa propriedade química (p>0,05). A dureza Knoop inicial foi maior para os grupos com 2,5 e 5% de triazina (p<0,05) e ambos os grupos apresentaram menor variação percentual de dureza Knoop após degradação em solvente. No presente estudo, foi produzida uma resina adesiva antibacteriana com agente sem liberação para o meio, capaz de copolimerizar com a blenda comonomérica, melhorando as propriedades do material restaurador.

Abstract The aim of this study was to formulate and evaluate an experimental adhesive resin with the addition of 1,3,5-triacryloylhexahydro-1,3,5-triazine at different concentrations. Experimental adhesive resins were obtained by mixing 50% wt bisphenol A glycol dimethacrylate (BisGMA), 25% wt triethylene glycol dimethacrylate (TEGDMA), 25% wt 2-hydroxyethyl methacrylate (HEMA) and photoinitiator system. The triazine compound was added in 1, 2.5 and 5% wt to a base adhesive resin and one group remained with no triazine as control group. The experimental adhesive resins were analyzed for antibacterial activity (n=3), degree of conversion (n=3) and softening in solvent (n=3). Data distribution was evaluated by Kolmogorov-Smirnov test, paired t test, one-way ANOVA and Tukey’s with a 0.05 level of significance. All groups with added triazine compound showed antibacterial activity against Streptococcus mutans (p<0.05). All groups achieved more than 70% degree of conversion, but there was no difference in this chemical property (p>0.05). The initial Knoop hardness was higher in 2.5 and 5% wt groups (p<0.05) and both groups present lower percentage variation of Knoop hardness after solvent degradation. The present study formulated an antibacterial adhesive resin with a non-releasing agent able to copolymerize with the comonomeric blend, improving the restorative material’s properties.

ABSTRACT Orthodontic treatment with fixed brackets plays a major role on the formation of white spot lesions. Objective This study aimed to incorporate silver nanoparticle solutions (AgNP) in an orthodontic adhesive and evaluate its physicochemical and antimicrobial properties. Material and Methods Silver nanoparticle solutions were added to a commercial adhesive in different concentrations (w/w): 0%, 0.11%, 0.18%, and 0.33%. Shear bond strength (SBS) test was performed after bonding metal brackets to enamel. Raman spectroscopy was used to analyze in situ the degree of conversion (DC) of the adhesive layer. The surface free energy (SFE) was evaluated after the measurement of contact angles. Growth inhibition of Streptococcus mutans in liquid and solid media was determined by colony-forming unit count and inhibition halo, respectively. One-way ANOVA was performed for SBS, DC, SFE, and growth inhibition. Results The incorporation of AgNP solution decreased the SBS (p<0.001) and DC in situ (p<0.001) values. SFE decreased after addition of 0.18% and 0.33% AgNP. Growth inhibition of S. mutans in liquid media was obtained after silver addition (p<0.05). Conclusions The addition of AgNP solutions to Transbond™ XT adhesive primer inhibited S. mutans growth. SBS, DC, and SFE values decreased after incorporation up to 0.33% AgNP solution without compromising the chemical and physical properties of the adhesive.